PA1010 is a high-performance long-chain polyamide derived 100 percent from renewable castor oil.
It offers a unique stiffness-to-weight ratio and exceptional chemical resistance.
With water absorption as low as 0.12%, it maintains superior dimensional stability compared to PA6 or PA66.
It excels in low-temperature toughness and impact resistance.
This eco-friendly material is a perfect alternative to petroleum-based nylons for high-end electronics, sports equipment, and precision industrial parts.
It provides reliable thermal management and flame retardancy for electrical housings.

ITEM	STANDARD	UNIT	RESULT
Tensile Strength	GB 1040-92	Mpa	60.7
Nominal strain at break	GB/T 1040	%	210.2
Flexural Strength	GB 9341-88	Mpa	79.22
Flexural Module	GB 9341-88	MPa	1598.34
Charpy impact strength	GB/T 1043-93	KJ/m2	88
Charpy notched impact strength	GB/T 1043-93	KJ/m2	21
Melt Flow Rate	GB 3682 230℃/2.16㎏	g/10min	3.5
Meling point	GB/T4608	℃	200