PA610 Bio-based is a sustainable high-performance polyamide derived from renewable castor oil. 
It contains over 60 percent bio-content, reducing the carbon footprint.
PA610 offers a superior balance of properties between PA6 and PA12.
It has much lower water absorption (1.5 percent) than PA6 or PA66.
This ensures excellent dimensional stability in humid environments.
With a melting point of 215 C and a density of 1.07 g/cm3 , it provides excellent oil resistance and toughness.
It is the best choice for automotive fuel lines, seal skeletons, and high-pressure hydraulic systems.

NO.	ITEM	UNIT	STANDARD	RESULT
1	Charpy Notch Impact	KJ/m2	GB/T 1043	8.14
2	Charpy Non-Notch Impact	KJ/m2	GB/T 1043	90.22
3	Tensile Strength	MPa	GB 1040	62.52
4	Elongation At Break	％	GB/T 1040	193.54
5	Flexural Strength	MPa	GB 9341	82.44
6	Flexural Module	MPa	GB 9341	1580.72
7	Melt Flow Rate	g/10min	GB 3682 230℃/2.16Kｇ	3.3
8	Transmittance	%	GB 1033	87.38
Remark