Nylon PA1010 -09 resin

Product description
PA1010 resin is used as a modified substrate to replace PA11 or PA12.
Performance parameters

Item	Test Standard	Unit	PA 1010 -09
Viscosity Number	GB/T 12006 / ISO 307	cm³/g	100±20
Melting Range	GB/T 16582 / ISO 3146	℃	202
Density	GB/T 1033 / ISO 1183	kg/m³	1040±10
Tensile Strength	GB/T 1040 / ISO 572-1/-2	MPa	>50
Tensile Modulus	GB/T 1040 / ISO 572-1/-2	MPa	>1000
Tensile Strain at Break	GB/T 1040 / ISO 572-1/-2	%	≥200
Charpy Unnotched Impact Strength(+23℃)	GB/T 1043 / ISO 179/1cA	kJ/m²	21
Charpy Notched Impact Strength(+23℃)	GB/T 1043 / ISO 179/1cA	kJ/m²	—

Performance characteristics
PA1010 resin has a low water absorption rate in nylon, good dimensional stability, oil and alkali resistance, and is non-toxic. It has ultra-high toughness, strong adhesion, high strength, low molding shrinkage, and good molding processing. It is mainly used as a modified substrate.
Application field
Mainly used for the production of automotive brake pipes, fuel pipes, corrugated pipes, automotive quick couplings, automotive ABS system sensor housings, and air conditioning hoses. It is also suitable for surface coating of wires, cables, optical cables, metals, or ropes.
It can be used for injection molding, extrusion, blow molding or powder coating according to customer requirements, and can replace PA11 widely used in industrial fields such as aerospace, shipbuilding, automotive, textile, instrumentation, electrical, medical equipment, etc.