It is a core barrier material for fuel lines.
It resists gasoline, diesel, and bio-fuels. PA610 has very low fuel absorption with less than 5 percent change after 1000 hours.
This stops the material from swelling or cracking.
The fuel permeation rate is very low at less than 0.1g per square meter every 24 hours.
It works from minus 40 to 120 Celsius for a 10-year life.
Processing: Injection mold at 230 to 260 Celsius. Use 60 to 90 Celsius mold temperature.
As a direct factory, we offer green solutions for sustainable fuel systems.
PA610 TDS:
| NO. | ITEM | UNIT | STANDARD | RESULT |
| 1 | Charpy Notch Impact | KJ/m2 | GB/T 1043 | 8.14 |
| 2 | Charpy Non-Notch Impact | KJ/m2 | GB/T 1043 | 90.22 |
| 3 | Tensile Strength | MPa | GB 1040 | 62.52 |
| 4 | Elongation At Break | ％ | GB/T 1040 | 193.54 |
| 5 | Flexural Strength | MPa | GB 9341 | 82.44 |
| 6 | Flexural Module | MPa | GB 9341 | 1580.72 |
| 7 | Melt Flow Rate | g/10min | GB 3682 230℃/2.16Kｇ |
3.3 |
| 8 | Transmittance | % | GB 1033 | 87.38 |
| Remark | ||||